PENINGKATAN NILAI UJI BULK DAN NILAI DAYA REGANG PADA MUTU KERTAS CETAK A
DOI:
https://doi.org/10.54314/jssr.v9i1.5718Abstract
Abstract: This study was conducted to determine the improvement of bulk and elongation in Printing Paper A made from cassava peel and oil palm fiber. Using an experimental method and a quantitative approach, the material composition variations were as follows: sample A (80%:20%), sample B (60%:40%), sample C (40%:60%), and sample D (20%:80%). The pulp-making process was carried out with chemical treatment using 3% NaOH and 3.5% HNO₃ solutions, followed by bleaching with 10% H₂O₂, then dried and formed into paper sheets. Characterization was conducted based on SNI 7274:2008. The bulk test results were 1.073 cm³/g for sample A, 1.088 cm³/g for sample B, 1.090 cm³/g for sample C, and 1.096 cm³/g for sample D. The elongation results were 1.589% for sample A, 0.682% for sample B, 2.800% for sample C, and 2.800% for sample D. This study shows that the higher the proportion of oil palm fiber, the more significant the contribution to the increase in bulk and elongation values of the paper. Keyword: Bulk, Cassava Peel, Elongation, Palm Fiber, Paper Abstrak: Penelitian ini dilakukan untuk menentukan peningkatan bulk dan daya regang pada kertas cetak A berbahan kulit ubi dan serat sawit. Dengan menggunakan metode eksperimen dan pendekatan kuantitatif, variasi komposisi bahan adalah sebagai berikut: sampel A (80%:20%), sampel B (60%:40%), sampel C (40%:60%), dan sampel D (20%:80%). Proses pembuatan pulp dilakukan dengan perlakuan kimia menggunakan larutan NaOH 3% dan HNO₃ 3,5%, dilanjutkan dengan pemutihan menggunakan H₂O₂ 10%, kemudian dikeringkan dan dicetak menjadi lembaran kertas. Karakterisasi dilakukan berdasarkan SNI 7274:2008. Hasil uji bulk adalah 1,073 cm3/g untuk sampel A, 1,088 cm3/g untuk sampel B, 1,090 cm3/g untuk sampel C, dan 1,096 cm3/g untuk sampel D. Hasil daya regang adalah 1,589% untuk sampel A, 0,682% untuk sampel B, 2,800% untuk sampel C, dan 2,800% untuk sampel D. Penelitian ini menunjukkan bahwa semakin tinggi peningkatan proporsi serat sawit memberikan kontribusi signifikan terhadap kenaikan nilai bulk dan daya regang kertas. Kata kunci: Bulk, Daya Regang, Kertas, Kulit Ubi, Serat SawitDownloads
References
Bayu Anugrah Kasa, E. J. (2023). Analisis Sifat Fisis Pembuatan Kertas Dari Serat Daun Nanas Dan Kulit Durian. Jurnal Kumparan Fisika, 6(2), 125–132. https://doi.org/10.33369/jkf.6.2.125-132
Dedi Kurniawan, A. (2020). Pemanfaatan Limbah Serat (Fiber) Buah Kelapa Sawit Dan Plastik Daur Ulang (Polypropylene) Sebagai Material Komposit Papan Partikel (Particle Board). Journal of Renewable Energy and Mechanics, 3(02), 60–70. https://doi.org/10.25299/rem.2020.vol3.no02.4884
Dharosno, W. W., & Pundu, A. (2020). Analisa Kuat Tarik pada Kertas Berbahan Dasar Serat Daun Nanas. Jurnal Teknologi Dan Rekayasa, 5(1), 46–56.
Irnawati. (2021). KAJIAN PEMBUATAN KERTAS DARI BERBAGAI SERAT LIMBAH KULIT NON-KAYU: STUDI KEPUSTAKAAN [Study of Paper Making from Various Fruit Skin Wastes: A Review]. J. Sains Dan Teknologi Pangan, 6(1), 3620–3628.
Kurniasari, A. E., & Widayatno, T. (2023). Pemanfaatan kulit singkong (Manihot Esculenta) sebagai bahan dasar pembuatan pulp dengan metode titrasi. Jurnal Sain Dan Teknik, 5(2), 102–110.
LUBIS, R., RIYANTO, R., & SAISA, S. (2024). Preparation and characterization of physical properties of molded pulp from empty fruit bunches of oil palm. Jurnal Natural, 24(2), 107–114. https://doi.org/10.24815/jn.v24i2.37444
Marlina, R., Sumantri, Y., Kusumah, S. S., Syarbini, A., Cahyaningtyas, A., Petanian, T. I., Ilmu, F., Halal, P., & Djuanda, U. (2021). Karakterisasi Komposit Biodegradable Foam Dari Kemasan Pangan. Jurnal Kimia Dan Kemasan, 43(1), 1–11.
Ningsih, M., Sirait, R., & Jumiati, E. (2023). Pengaruh Nilai Ketahanan Tarik Terhadap Daya Regang Dalam Pembuatan Kertas Dari Bahan Baku Kulit Singkong dan Daun Nanas. Jurnal Fisika Unand, 12(4), 518–https://doi.org/10.25077/jfu.12.4.518-525.2023
Rahayu, S., Wirjosentono, B., Oktavia, E., Zuhra, C. F., Piliang, A. F. R., Pasaribu, K. M., Bibina, R. A., Goei, R., Tok, A. I. Y., Dellyansyah, Saputra, A. M. A., & Gea, S. (2024). Improved mechanical and thermal performance of bacterial cellulose paper through cationic cassava starch addition. South African Journal of Chemical Engineering, 50(April), 379–387. https://doi.org/10.1016/j.sajce.2024.09.003
Ramayanti, C., Sari, W. F., Oktaviani, E. D., & Mujiyanti, A. (2024). Pemanfaatan Limbah Tandan Kosong Kelapa Sawit dan Kulit Jagung Manis menjadi Kertas Karton menggunakan Metode Organosolv [ Utilization of Empty Fruit Bunch and Sweet Corn Husk Waste into Paperboard using the Organosolv Method ]. 10(3), 216–223.
Rohmawati, L., & Suaebah, E. (2025). ANALISIS KARAKTERISTIK KOMPOSIT PULP KERTAS DAN SERABUT KELAPA. 14, 141–151.
Sembiring, Haris Marturia, Mohammad Prasanto Bimantio, R. A. W. (2023). Penggunaan Serat Mesokarp Kelapa Sawit Sebagai Pengganti Serat Sintetis Pada Pembuatan Komposit Fiberglass The use of Oil Palm Mesocarp Serat as a Substitute for Synthetic Serat in the Manufacture of Fiberglass Composites. Kelapa Sawit, 2023(2), 70–81.
Trianah, Y. (2022). Pengaruh Penambahan Serabut (Fiber) Kelapa Sawit Terhadap Porositas Beton. Jurnal Teknik Sipil Cendekia (Jtsc), 3(2), 28–37. https://doi.org/10.51988/jtsc.v3i2