PENINGKATAN PENYERAPAN GELOMBANG MIKRO PADA BARIUM HEKSAFERRIT DENGAN DOPING YTTRIUM (Y)
DOI:
https://doi.org/10.54314/jssr.v9i2.6113Kata Kunci:
Barium Hexafere, Yttrium, solid state reaction, XRD, SEM, VNAAbstrak
Abstract:This study discusses the effect of Yttrium (Y) doping variations on the physical and electromagnetic properties of Barium Hexafere (BaFe??O??) synthesized using the solidstate reaction method. The doping variations used were 0.00; 0.01; 0.03; and 0.05 at%. The calcination process was carried out at 600 °C and sintering at 1200 °C. Characterization was performed using X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Vector Network Analyzer (VNA). The XRD results showed that all samples had a single phase of BaFe??O?? with a hexagonal structure according to JCPDS No. 84-0757 without secondary phases, with the highest crystallinity at a doping of 0.05 at%. SEM analysis showed an increase in grain density and a decrease in porosity with increasing Y doping. VNA testing showed the best Reflection Loss value of –12.98 dB at a frequency of 8.87 GHz with 71.8% microwave absorption. Yttrium doping of 0.05 at% is the optimal composition for enhancing microwave absorption in Barium Hexafere.
Keywords:Barium Hexafere, Yttrium, solid state reaction, XRD, SEM, VNA
Abstrak: Penelitian ini membahas pengaruh variasi doping Yttrium (Y) terhadap sifat fisis dan elektromagnetik Barium Heksaferrit (BaFe??O??) yang disintesis menggunakan metode solid state reaction. Variasi doping yang digunakan yaitu 0,00; 0,01; 0,03; dan 0,05 at%. Proses kalsinasi dilakukan pada suhu 600 °C dan sintering pada suhu 1200 °C. Karakterisasi dilakukan menggunakan X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), dan Vector Network Analyzer (VNA). Hasil XRD menunjukkan semua sampel memiliki fasa tunggal BaFe??O?? dengan struktur heksagonal sesuai JCPDS No. 84-0757 tanpa fasa sekunder, dengan kristalinitas tertinggi pada doping 0,05 at%. Analisis SEM menunjukkan peningkatan kerapatan butir dan penurunan porositas seiring bertambahnya doping Y. Uji VNA menunjukkan nilai Reflection Loss terbaik –12,98 dB pada frekuensi 8,87 GHz dengan penyerapan gelombang mikro 71,8%. Doping Yttrium 0,05 at% merupakan komposisi optimal untuk meningkatkan kemampuan penyerapan gelombang mikro pada Barium Heksaferrit.
Kata kunci: Barium Heksaferrit, Yttrium, solid state reaction, XRD, SEM, VNA
Unduhan
Referensi
Batubara, D. A., Fazirah, C., Syahfitrih, L., Fadilla, M., & Anggraini, R. (2023). Pengaruh Radiasi Elektromagnetik Yang Ditimbulkan Oleh Telepon Seluler. Al-Irsyad Journal of Physics Educations, 2(2), 76–85.
Ridwan, M., & Nasution, N. (2025). Pengaruh Doping Yttrium terhadap Kinerja Penyerapan Gelombang Mikro pada Barium Heksaferrit. JISTech (Journal of Islamic Science and Technology) JISTech, 10(2), 208–211. https://doi.org/10.30829/jistech.v10i2.28639
Seniari, N. M., & Dharma, B. W. (2020). Penyuluhan Bahaya Radiasi Gelombang Elektromagnetik Pada Organ Tubuh Mahluk Hidup Di Kelurahan Pagutan Barat Mataram. Seminar Nasional Pengabdian Kepada Masyarakat Tahun 2020 Prosiding PEPADU 2020, 2, 230–235.
Sihotang, M. S., Angelo, M. A., Naibaho, M., Maulidita, M., Ichsan, N., & Ginting, M. (2025). Effect of Barium Hexaferrite Doped Yttrium (Y3+) On The Microwave Absorption By Solid-State Reaction Methods. Journal of Technomaterial Physics, 7(1), 063–070. https://doi.org/10.32734/jotp.v7i1.19265
Syukur Ziliwu, H., Juang, F., Waruwu, P., & Gulo, F. A. (2025). Analisis Literatur Tentang Gelombang Elektromagnetik Dan Pengaruhnya Pada Teknologi Komunikasi. IDENTIK: Jurnal Ilmu Ekonomi, Pendidikan Dan Teknik, 02(06), 13–18.
Yassin, M. F., Nazara, B. R. J., Qiblatain, D., Azhary, K. M. R., Andika, M. R., Hidayatulloh, F. A., & Lubis, B. O. (2024). Implementasi Algoritma C4.5 Untuk Analisis Dampak Negatif Gelombang Elektromagnetik Telepon Seluler Terhadap Otak Pada Periode 2019-2023. Jurnal Humaniora Dan Sosial Sains, 2(1), 23–30.
Yustanti, E., Trisdian, A., & Noviyanto, A. (2024). Pengaruh Amplitudo Dan Waktu Sonikasi Terhadap Penurunan Reflection Loss Pada Sintesis Material Absorber Berbasis Pasir Besi Banten Untuk Aplikasi Pesawat Anti Radar. Jurnal Integrasi Proses, 13(1), 13–20. http://jurnal.untirta.ac.id/index.php/ji
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
Hak Cipta (c) 2026 Annisa Salsabila, Nazaruddin Nasution, Masthura
Artikel ini berlisensiCreative Commons Attribution-ShareAlike 4.0 International License.